For more than 50 years, ELANTAS PDG, Inc. has had products for tooling and prototyping. With the addition of the CONAP® business from Solvay, we have expanded our expertise in formulating epoxy and polyurethane resins in liquid and solid form. Our customers benefit from our know-how and long-term experience.
Depending on your individual requirements, we offer different search and selection functions to help you find the appropriate material. The listed products are an extract from our actual product portfolio. More products are available on request.
Do you need further information about our tooling materials? Please get in touch with us. We are looking forward to your email to info.ELANTAS.PDG@altana.com.
To download a Technical Data Sheet or a Material Safety Data Sheet, please clicke here.
Product | Mix Ratio by Weight A/B | Part A Viscosity @ 25°C | Part B Viscosity @ 25°C | Initial Mixed Viscosity @ 25°C | Work Life @ 25°C | Shore Hardness | Tensile Strength PSI | Ultimate Elongation | Tear Strength PLI | Cure Time | Key Benefits |
Conathane® TU-801 | 100/51 | 8,500 | 350 | 3,500 | 20-30 min | 80A | 3,500 | 700% | 360 | 16 hrs @ 80°C 7-21 days @ 25°C | UV Stabilized |
Conathane® TU-901 | 100/44 | 8,500 | 450 | 3,000-5,000 | 20-30 min | 90A | 4,000 | 750% | 400 | 16 hrs @ 80°C 7-21 days @ 25°C | UV Stabilized |
Conathane® TU-79MF | 100/45 | 5,000 | 1500 | 4,000 | 25-35 min | 75-80A | 1,800 | 750% | 325 | 1 hr @ 25°C + 16 hrs @ 80°C 7 days @ 25°C | Flexible elastomer system |
Conathane® TU-89MF | 100/53 | 7,000 | 1700 | 4,000 | 15-25 min | 89A | 3,200 | 600% | 425 | 1 hr @ 25°C + 16 hrs @ 80°C 7 days @ 25°C | Flexible elastomer system |
Conathane® TU-8080 | 100/30 | 7,000 | 120 | 3,900 | 20-25 min | 80A | 3,500 | 875% | 464 | 7-10 days @ 25°C 16 hrs @ 80°C | Flexible elastomer system |
Conathane® TU-8090 | 100/20 | 4,200 | 356 | 3,500 | 15-20 min | 90A | 3,500 | 600% | 525 | 7-10 days @ 25°C 16 hrs @ 80°C | Pourable in almost any configuration |
Conathane® TU-956-1 | 100/28 | 5,500 | 900 | 5,000 | Pot: 8 min | 55D | 2,800 | 390% | 480 | -- | Pourable in almost any configuration |
Conathane® TU-981 | 100/60 | 2,800 | 190 | 2,000 RT 1,200 @ 60°C | 16-20 min RT 10 min @ 60°C | 65D | 4,050 RT 4,500 @ 60°C | 230% RT 175% @ 60°C | 600 | 7 days @ RT 16 hrs @ 60°C | Rotocasting applications |
Product | Type | IPC-CC-830B Certified | MIL-I-46058C Qualified | UL Certified | Single/Two-Component | Tack-Free @ 25°C | System Viscosity @ 25°C | Key Benefits |
CONAP® CE 1170 | AR | Yes | Yes | Yes | 1 | 15 min | 400 | Hydrolytic stability w/o compromising flexibility |
CONAP® CE 1171 | AR | Yes | Yes | Yes | 1 | 20 min | 900 | Humidity resistance & hydrolytic stability |
Product | Mix Ratio by Weight A/B | Part A Viscosity @ 25°C | Part B Viscosity @ 25°C | Initial Mixed Viscosity @ 25°C | Work Life /Gel @ 25°C | Shore Hardness | Tensile Strength PSI | Elon-gation | Tear Strength PLI | Flammability (UL 94) | Thermal Conductivity (W/mK) | Exotherm °C/mass size, grams | Key Benefits |
Conacure® EA-02 | Varies | 58,000 | 55 | Varies | Varies | Varies | Varies | -- | -- | 94 V-0 | Varies | Varies | Room temperature cure, low viscosity, rigid castings |
Conacure® EA-028 | Varies | 58,000 | 36 | Varies | Varies | Varies | Varies | -- | -- | 94 V-0 | Varies | Varies | Limited flexibility, low viscosity, cures in thin films at room temperature, good thermal shock resistance |
Conacure® EA-87 | Varies | 58,000 | 60 | Varies | Varies | Varies | Varies | -- | -- | 94 V-0 & 94-5VA | Varies | Varies | Limited flexibility, low viscosity, less expensive than EA-028 |
Conapoxy® FR-1046 | Varies | 17,000 | Varies | Varies | Varies | 85-90D | Varies | -- | -- | -- | Varies | Varies | Low viscosity, low exotherm, excellent thermal shock resistance |
Conapoxy® FR-1047 | Varies | 58,000 | Varies | Varies | Varies | Varies | Varies | -- | -- | At least 94V-0 | Varies | Varies | Low exotherm, good electrical properties |
Conapoxy® FR-1080 | 100/83 | 4,000 | 300 | 300 | > 2 hrs | 90D | 8,200 | 2% | 250 | -- | -- | -- | -- |
Conapoxy® FR-1210 | Varies | 95,000 | Varies | Varies | Varies | 80-90D | Varies | -- | -- | -- | Varies | -- | Good resistance to mechanical and thermal shock, good electrical properties |
Conapoxy® FR-1274 | 100/100 | 27,000 | 55000 | 40000 | 2-3 hrs (0.5lbs) | 80D | 5,500 | -- | -- | 94V-0 | 0.84 | 43°C (200g) | Low cost, low exotherm, low shrinkage |
Conapoxy® FR-1810 | 100/100 | 7,000 | 14000 | 8000 | 80 min (200g) | 80-85D | 1,325 | 22% | -- | 94V-0 | 0.7025 | 36°C (225g) | Low exotherm, excellent handling properties |
Conapoxy® FR-1820 | 100/25 | 22,000 | 1960 | 6900 | 15-18 min (150g) | 80-85D | 4,880 | 3% | -- | 94V-0 | 0.4970 | -- | RoHs compliant |
Conapoxy® FR-1830 | 100/200 | 14,000 | 85 | 2190 | 50 min (50g) | 80-85D | 5,200 | -- | -- | 94V-0 | 0.4917 | 73°C (225g) | RoHs compliant, can be shipped to EU when cured (restricted when not cured) |
Conapoxy® RN-1000 | Varies | 800 | Varies | Varies | Varies | Varies | Varies | -- | -- | -- | Varies | -- | Low shrinkage, low exotherm, good thermal shock resistance, good electrical properties |
Conapoxy® RN-1200 | Varies | 10,000 | Varies | Varies | Varies | Varies | Varies | -- | -- | -- | Varies | -- | Low viscosity, low shrinkage, low exotherm, good thermal shock resistance, good electrical properties |
Product | Mix Ratio by Weight | Part A Viscosity @ 25°C | Part B Viscosity @ 25°C | Gel Time @ 25°C | Mixed Viscosity @ 25°C | Hardness | Tensile Strength | Elongation | Tear Strength | Linear Shrinkage | Key Benefits |
| CONAP® UC-23 | 100/20 | 10,000 | 650 | 1 lb = 40 min | 3,500 | 80 ± 5 D | 5,300 | 20% | 350 | 0.006 | High tensile strength, good abrasion resistance |
Product | Mix Ratio by Weight | Part A Viscosity @ 25°C | Part B Viscosity @ 25°C | Gel Time @ 25°C | Mixed Viscosity @ 25°C | Hardness | Tensile Strength | Elongation | Tear Strength | Linear Shrinkage | Key Benefits |
CONAP® UC-23 | 100/20 | 10,000 | 650 | 1lb = 40min | 3500 | 80 ± 5 D | 5,300 | 20% | 350 | 0.006 | High tensile strength, good abrasion resistance |
Conathane® UC-40 | 100/50 | 120 | 1400 | 200g = 12min | 500 | 80D | 5,100 (cured @ RT) 7,000 (cured @ 80°C) | 6% (cured @RT) 8% (cured @80°C) | NA | 0.003 | High impact resistance and excellent machineability |
Conathane® UC-41 | 100/50 | 95 | 1400 | 200g = 4min | 500 | 80D | 5,500 (cured @ RT) 7,500 (cured @ 80°C) | 6% (cured @RT) 7% (cured @80°C) | NA | 0.0046 | High impact resistance and excellent machineability |
Conathane® UC-43 | 100/50 | 450 | 2200 | 200g = 15min | 1000 | 85D (cured @ RT) 80D (cured @ 93°C) | 6,000 (cured @ RT) 8,500 (cured @ 80°C) | 6% (cured @RT) 7% (cured @80°C) | NA | 0.0055 | Easy to use, easy to color |
Conathane® UC-54 AFL | 100/68 | 725 | 1415 | 200g = 10-15min | 1000 | 80D | NA | NA | NA | NA | -- |
Conathane® UC-54 | 100/50 | 500 | 2000 | 150g = 45min | 1200 | 85D (cured @ RT) 80D (cured @ 93°C) | 12,265 | 7-10% | NA | 0.450 | Casting of large parts, low exotherm |
Product | Color | Viscosity @ 25°C | SPG @ 25°C | Recommended Substrates | Recommended Thinners | Key Benefits |
CONAP® AD-1146 | Amber | 2,000 | 0.9 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | Bonds have high strength, excellent resistance to hydrolysis and environmental extremes |
CONAP® AD-1146-C | Amber | 160 | 0.86 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | -- |
CONAP® AD-1146-C-1 | Red | 160 | 0.86 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | -- |
CONAP® AD-1147 | Amber | 2,000 | 0.9 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | Bonds have high strength, excellent resistance to hydrolysis and environmental extremes |
CONAP® AD-1147-C | Amber | 160 | 0.86 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | -- |
CONAP® AD-1147-C-1 | Red | 160 | 0.86 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | -- |
CONAP® AD-1147-1 | Red | 2,000 | 0.9 | Aluminum alloys, magnesium, iron, steel, glass, glass-fiber laminates, wood, leather | S-1 | -- |
CONAP® AD-1161 | Light Amber | 80 | 0.881 | PVC | Methyl Ether Ketone (MEK) | Used for bonding polyurethanes to polyvinyl chlorides (PVC) during the curing process |
CONAP® PR-1167 | Light Amber | 76 | -- | Cured/liquid polyurethanes, neoprene rubber, cadmium-plated metals, etc. | -- | Remains flexible, does not turn to a rigid state |
Product | Appearance/Color | Products Recommended | Key Benefits |
CONAP® DS-1831A | Red | Epoxy & Urethane Systems | Ultimate resistance to heat and light |
CONAP® DS-1832 | Black | Epoxy & Urethane Systems | Ultimate resistance to heat and light |
CONAP® DS-1833 | Blue | Epoxy & Urethane Systems | Ultimate resistance to heat and light |
CONAP® DS-1836 | White | Epoxy & Urethane Systems | Ultimate resistance to heat and light |
Product | Appearance | SPG @ 25°C | Key Benefits |
CONAP® S-1 | Water White | 0.825 - 0.845 | Also used in clean up |
CONAP® S-8 | Water White | 0.90 - 0.92 | RoHS compliant |
CONAP® S-13 | Water White | 0.85 - 0.88 | Also used in clean up |
CONAP® S-22 | Water White | 0.90 - 0.93 | -- |